Blenda de PEUAPM/PET: obtenção e caracterização mecânica
| dc.contributor.advisor | Sousa, Alexandre Rangel de | |
| dc.contributor.advisorLattes | http://lattes.cnpq.br/9897600291568251 | |
| dc.contributor.author | Alves, Ivis Fernanda Teles | |
| dc.contributor.authorLattes | http://lattes.cnpq.br/7752065320406944 | |
| dc.contributor.referee | Calado, Claudinei Rezende | |
| dc.contributor.referee | Patrício, Patrícia Santiago de Oliveira | |
| dc.date.accessioned | 2025-04-24T12:30:45Z | |
| dc.date.available | 2025-04-24T12:30:45Z | |
| dc.date.issued | 2014-01-16 | |
| dc.description.abstract | Este estudo objetivou o desenvolvimento de blendas por meio da mistura de polietileno de ultra-alto peso molecular (PEUAPM) com poli(tereftalato de etileno) (PET), processadas por meio de compressão térmica, com intuito de avaliar as propriedades mecânicas de resistência à tração, impacto e desgaste. Foi avaliada ainda, a influência da massa molar nas propriedades mecânicas das blendas utilizando dois tipos de PEUAPM; um com massa molar de 8,0x106 g/mol e o outro com 3,0x106 g/mol. As amostras da blenda foram produzidas com as seguintes proporções: 90%PEUAPM/10%PET; 80%PEUAPM/20%PET e 70%PEUAPM/30%PET. As amostras foram caracterizadas pelos ensaios de tração, impacto e desgaste. Foi realizada ainda a caracterização térmica dos polímeros puros PET e PEUAPM por Calorimetria Exploratória Diferencial DSC; a caracterização da microestrutura da superfície de fratura após o ensaio de tração via Microscopia Eletrônica de Varredura (MEV) e, finalmente, a avaliação da absorção de água pelas blendas desenvolvidas. A adição de PET na blenda leva a um decréscimo nas propriedades de tensão de ruptura, deformação na ruptura, tenacidade e resiliência em comparação com o PEUAPM puro. Em relação à massa molar, o PEUAPM de maior massa molar (A) obteve uma redução percentual nos valores de tensão na ruptura menor do que o de menor massa molar (B) até a adição de 20%PET na blenda. A deformação na ruptura apresentou uma redução brusca para as duas massas molares, sem variação significativa entre elas. No ensaio de impacto realizado, não ocorreu rompimento dos corpos de prova; as amostras submetidas ao ensaio de desgaste não apresentaram desgaste significativo pelo período estudado. | |
| dc.description.abstractother | This study aimed to develop blends by mixing polyethylene of ultra -high molecular weight (UHMWPE ) with poly ( ethylene terephthalate ) ( PET ) , processed by thermal compression to obtain the mechanical properties of tensile strength , impact and wear. With molar ratio of 8.0 x106 g / mol mass and the other with 3.0 x106 g / mol, molar mass of the influence on the mechanical properties of the blends using two types of UHMWPE was also evaluated. Samples of the blends were produced with the following proportions of the two polymers: 90% PEUAPM/10% PET, 80% UHMWPE / PET 20% and 70% PEUAPM/30% PET. The mechanical properties were characterized by tensile, impact and wear. Thermal characterization of pure PET and UHMWPE polymers by differential scanning calorimetry DSC was also performed , to characterize the microstructure of the fracture surface after the tensile test via Scanning Electron Microscopy (SEM ) and finally , evaluating the water absorption of the blends developed . The addition of PET in the blend leads to a decrease in the properties of tensile strength, elongation at break, toughness and resilience compared to the pure UHMWPE. In relation to the molecular weight, the higher the molar mass of UHMWPE (A) had a percent reduction in the tensile values lower than the lower molar mass (B) by the addition of 20% PET blend at break . The elongation at break showed a marked reduction for the two molar masses, with no significant difference between them. In impact tests performed, there was no disruption of the specimens, samples subjected to wear test showed no significant wear the studied period. | |
| dc.identifier.uri | https://repositorio.cefetmg.br//handle/123456789/1264 | |
| dc.language.iso | pt | |
| dc.publisher | Centro Federal de Educação Tecnológica de Minas Gerais | |
| dc.publisher.country | Brasil | |
| dc.publisher.initials | CEFET-MG | |
| dc.publisher.program | Programa de Pós-Graduação em Engenharia de Materiais | |
| dc.subject | Polímeros | |
| dc.subject | Reciclagem | |
| dc.subject | Polietileno | |
| dc.subject | Blendas | |
| dc.title | Blenda de PEUAPM/PET: obtenção e caracterização mecânica | |
| dc.type | Dissertação |