Estudo da influência da espessura da camada de shop primer sobre a estabilidade do arco elétrico e das características do metal de soldas produzidas pelo processo FCAW sobre chapas revestidas

Página do item simplificado
dc.contributor.advisorVaz, Cláudio Turani
dc.contributor.advisor-coSilva, Bruno Cordeiro
dc.contributor.advisor-coLatteshttp://lattes.cnpq.br/1868816663610134
dc.contributor.advisorLatteshttp://lattes.cnpq.br/5386844601893935
dc.contributor.authorVerde, Lorena Arco
dc.contributor.authorLatteshttp://lattes.cnpq.br/4622502189914306
dc.contributor.refereeVaz, Cláudio Turani
dc.contributor.refereeSilva, Bruno Cordeiro
dc.contributor.refereeCastro, Carlos Alberto Carvalho
dc.contributor.refereeCosta, Maria Celeste Monteiro de Souza
dc.date.accessioned2025-03-13T16:52:05Z
dc.date.available2025-03-13T16:52:05Z
dc.date.issued2024-05-23
dc.descriptionAkzo Nobel, Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - Brasil (CAPES) - Código de financiamento 001
dc.description.abstractNa indústria metal mecânica, o principal objetivo é alcançar maior produtividade com o menor custo de fabricação. Para atingir tal eficiência, é necessário acompanhar o processo de fabricação de perto. Quantidades consideráveis de material metálico são desperdiçadas devido a perdas e retrabalho causados pela corrosão. Em setores como a indústria naval e offshore, o tempo de processamento e a localização agravam a corrosão, tornando indispensável a proteção do material. O shop primer (tinta de pré-construção) é um grande aliado nesse processo, pois impede o contato direto com o metal base, criando uma barreira protetiva contra a corrosão. A soldagem FCAW (Flux-cored Arc Welding) é amplamente utilizada nessas situações por ser uma das alternativas mais produtivas. No entanto, a qualidade das soldas produzidas por esse processo pode ser comprometida quando realizadas sobre a camada protetiva. Este trabalho teve como objetivo verificar a influência de diferentes espessuras de shop primer aplicado em chapas de aço carbono ASTM A-36 no processo de soldagem e nas características das soldas produzidas pelo arame classe E71T1-C1A2-CS2. Foram realizadas soldagens com monitoramento da corrente e tensão, além de análises macro e microestruturais e das escórias das soldas. Maiores espessuras da camada de shop primer resultaram em aumento na largura e penetração das soldas. O monitoramento dos parâmetros elétricos durante a soldagem não indicou alterações no arco elétrico nas diferentes condições avaliadas. Alterações na diluição, resultantes do aumento na penetração, não impactaram a microestrutura do metal de solda. Medidas do ângulo de contato do cordão e a análise da escória, juntamente com a análise dos sinais elétricos, indicaram que a espessura da camada de shop primer foi responsável pela alteração na fluidez do metal líquido na poça de fusão.
dc.description.abstractotherIn the metal-mechanical industry, the main goal is to achieve higher productivity at the lowest manufacturing cost. To attain such efficiency, it is necessary to closely monitor the manufacturing process. Considerable amounts of metallic material are wasted due to losses and rework caused by corrosion. In sectors such as the naval and offshore industries, processing time and location exacerbate corrosion, making material protection indispensable. Shop primer (pre-construction paint) is a great ally in this process, as it prevents direct contact with the base metal, creating a protective barrier against corrosion. FCAW (Flux-cored Arc Welding) is widely used in these situations as it is one of the most productive alternatives. However, the quality of the welds produced by this process can be compromised when performed over the protective layer. This study aimed to verify the influence of different thicknesses of shop primer applied to ASTM A-36 carbon steel plates on the welding process and the characteristics of welds produced by the E71T1-C1A2-CS2 class wire. Weldings were performed with monitoring of current and voltage, as well as macro and microstructural analyses and slag analyses of the welds. Greater thicknesses of the shop primer layer resulted in increased weld width and penetration. Monitoring of electrical parameters during welding did not indicate changes in the electric arc under the different conditions evaluated. Changes in dilution, resulting from increased penetration, did not impact the microstructure of the weld metal. Measurements of the bead contact angle and slag analysis, along with the analysis of electrical signals, indicated that the thickness of the shop primer layer was responsible for altering the fluidity of the molten metal in the weld pool.
dc.identifier.urihttps://repositorio.cefetmg.br//handle/123456789/749
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia de Materiais
dc.subjectSoldagem
dc.subjectArames tubulares
dc.subjectTintas para revestimentos
dc.subjectCorrosão e anticorrosivos
dc.titleEstudo da influência da espessura da camada de shop primer sobre a estabilidade do arco elétrico e das características do metal de soldas produzidas pelo processo FCAW sobre chapas revestidas
dc.typeDissertação

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Estudo da influência da espessura da camada de shop primer sobre a estabilidade do arco elétrico e das características do metal de soldas produzidas pelo processo FCAW sobre chapas revestidas.pdf
Tamanho:
3.38 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.39 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia de Materiais