Estudo das transformações macro e microestruturais das juntas soldadas do Aço SAE - 4340 pelo processo FCAW

Página do item simplificado
dc.contributor.advisorCosta, Maria Celeste Monteiro de Souza
dc.contributor.advisor-coPereira, Wanderley Xavier
dc.contributor.advisor-coLatteshttp://lattes.cnpq.br/2710795181589959
dc.contributor.advisorLatteshttp://lattes.cnpq.br/8178787669759338
dc.contributor.authorOliveira, Fabiano Farias de
dc.contributor.authorLatteshttp://lattes.cnpq.br/3360384807973461
dc.contributor.refereeCorrea, Elaine Carballo Siqueira
dc.contributor.refereeCastro, Carlos Alberto Carvalho
dc.date.accessioned2025-04-15T11:42:28Z
dc.date.available2025-04-15T11:42:28Z
dc.date.issued2015-11-04
dc.description.abstractO processo de soldagem com arame tubular (FCAW) vem ganhando espaço no mercado, principalmente devido a sua alta produtividade, pois este processo apresenta grande facilidade de ser mecanizado/automatizado. Outra característica importante que destaca neste processo é a possibilidade de soldar a maioria dos metais. Esta facilidade se dá em função da liberdade de produzir arames com composições químicas bem específicas. Porém, na soldagem de aços temperáveis tem-se um grande desafio que é o controle da microestrutura gerada pelos diferentes ciclos térmicos gerados durante a soldagem. Em função desta particularidade e por haver poucos estudos nesta área, o objetivo deste trabalho é analisar os efeitos térmicos do processo de soldagem FCAW, nas propriedades metalúrgicas e geométricas da região soldada para o aço transformável SAE4340. Para o desenvolvimento deste trabalho foi considerado como variáveis de controle, a corrente de soldagem; a tensão de soldagem; os tratamentos de pré e pós-aquecimento e a peça sem tratamento. A finalidade do estudo dos parâmetros de controle é apontar as melhores condições experimentais que proporcionam uma zona termicamente afetada (ZTA) com menor percentual de fases duras como bainita e a martensita, além de promover uma boa geométrica do cordão de solda que garantam as propriedades mecânicas. Os resultados deste trabalho mostraram que as soldas executadas com correntes mais elevadas e nas condições de pré e pós-aquecimento apresentaram condições mais favoráveis em relação aos aspectos geométricos do cordão, como: penetração, reforço, diluição e principalmente evitou a formação de partículas duras, como a martensita e bainita.
dc.description.abstractotherThe welding process with tubular wire (FCAW) has gained space in the Market, mainly due to its high productivity because such a process presents great facility to be mechanized/automated. Another important feature in this process is the possibility of welding the majority of metals. This facility is due to the fact that it is possible to produce wires with chemical compositions very well specified. Nevertheless, in the welding process of hardenable steels there is a great challenge in controlling the microstructure generated during the different thermal cycles. In function of this particularity and because there are a few studies in this area, the objective of this study is to analyze the thermal effects in the FCAW welding process in the metallurgical and geometrical properties of the welded region for the transformable steel 4340. For the development of this study, the principal variables considered were the current and the tension of the arc, with and without pre and post annealing. The target of this control is to point out the best experimental conditions that would lead to a heat affected zone (ZAT) with less percentage of hard phases such as bainite and martensite, besides promoting a good geometry of the weld beam, in order to grant good mechanical properties. The results of this study demonstrate that the weld executed with higher current values and in the conditions of pre and post-welding presented more favorable conditions relating to the geometric aspects of the weld beam such as penetration, reinforcement, dilution and mainly avoided the formation of hard particles such as martensite and bainite.
dc.identifier.urihttps://repositorio.cefetmg.br//handle/123456789/1198
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia de Materiais
dc.subjectSoldagem
dc.subjectAço (Tratamento térmico)
dc.subjectMicroestrutura
dc.titleEstudo das transformações macro e microestruturais das juntas soldadas do Aço SAE - 4340 pelo processo FCAW
dc.typeDissertação

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Estudo das transformações macro e microestruturais das juntas soldadas do Aço SAE - 4340 pelo processo FCAW.pdf
Tamanho:
5.7 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.39 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia de Materiais