Avaliação das propriedades de verniz para madeira a base de dispersão aquosa de poliuretano

Página do item simplificado
dc.contributor.advisorPatrício, Patrícia Santiago de Oliveira
dc.contributor.advisor-coAyres, Eliane
dc.contributor.advisor-coLatteshttp://lattes.cnpq.br/1370798140664840
dc.contributor.advisorLatteshttp://lattes.cnpq.br/5625112455084806
dc.contributor.authorAlves, Taciana Marina Reis
dc.date.accessioned2023-06-05T13:54:17Z
dc.date.available2023-06-05T13:54:17Z
dc.date.issued2017
dc.description.abstractNeste trabalho, um grupo de dispersões aquosas de poliuretanos a partir da mistura de dióis, polipropileno glicol (PPG) e policarbonato (PC) foi sintetizado. As propriedades mecânicas e estruturais dos filmes produzidos foram estudadas. A substituição parcial e total de PPG por PC influencia significativamente nas propriedades mecânicas dos filmes obtidos das dispersões aquosas de poliuretano, sendo que aqueles preparados a partir da mistura de polióis são superiores as dos polímeros preparados apenas com PPG’s. Foi observado que a inserção de até 75% em massa de policarbonato como diol resultou em poliuretanos mais dúcteis e resistentes, gerando materiais com propriedades mecânicas melhores. Os revestimentos foram aplicados na madeira e os corpos de prova tiveram suas propriedades de transparência e proteção, quando submetidos ao ensaio de envelhecimento frente à radiação UV, avaliados. Nas amostras de madeira revestidas com os diferentes vernizes poliuretânicos após a exposição à radiação UV por 15 e 30 dias, fica perceptível que aquelas revestidas com as formulações que contêm maior teor de policarbonato, tiveram menor alteração na sua cor. Através de experimentos de envelhecimento acelerado e colorimetria foi sugerido que a presença de policarbonato interfere discretamente na degradação da madeira, já agindo como agente de proteção, porém a necessidade de melhorias fez com que fosse realizada a adição de cargas (oxihidróxido de nióbio). A adição de cargas ao PU 75 gerou filmes com melhor resistência a degradação UV.
dc.description.abstractotherIn this work, a group of aqueous dispersions of polyurethanes from a mixture of diols, polypropylene glycol (PPG) and polycarbonate (PC) was synthesized. The mechanical and structural properties of the films produced were studied. A partial and total substitution of PPG by PC significantly influences the mechanical properties of the films obtained from the aqueous polyurethane dispersions, wherein they are prepared from the polyol mixture are superior as the polymers prepared with only PPG's. It was observed that the insertion of up to 75% by mass of polycarbonate as a diol resulted in more ductile and resistant polyurethanes, generating materials with better mechanical properties. The coatings were applied to the wood and the specimens with their good transparency and protection when subjected to the aging test against UV radiation. In wood samples coated with the different polyurethane varnishes after exposure to UV radiation for 15 and 30 Days, and it is noticeable that those coated with formulations containing the higher polycarbonate content had less amount in their color. Accelerated aging and colorimetry experiments have suggested that the presence of polycarbonate interferes discreetly in the degradation of the wood, already acting as a protective agent, but a need for improvements has led to the addition of bodywork (niobium oxyhydroxide). The addition of fillers to PU 75 generated films with better resistance to UV degradation.
dc.identifier.urihttps://repositorio.cefetmg.br/handle/123456789/215
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia Civil
dc.subjectMadeira - Preservativos
dc.subjectPoliuretanas
dc.subjectCompostos de nióbio
dc.titleAvaliação das propriedades de verniz para madeira a base de dispersão aquosa de poliuretano
dc.typeThesis
dspace.entity.type

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Avaliacao das propriedades de verniz para madeira a base de dispersao aquosa de poliuretano_Dissertacao.pdf
Tamanho:
1.53 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.71 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia Civil