Influência das temperaturas de pré e pós-aquecimento de soldagem sobre as características microestruturais e mecânicas da zona termicamente afetada em ferro fundido nodular

Página do item simplificado
dc.contributor.advisorVaz, Cláudio Turani
dc.contributor.advisor-coCosta, Maria Celeste Monteiro de Souza
dc.contributor.advisor-coLatteshttp://lattes.cnpq.br/8178787669759338
dc.contributor.advisorLatteshttp://lattes.cnpq.br/5386844601893935
dc.contributor.authorSantos, Diêgo Naron
dc.contributor.authorLatteshttp://lattes.cnpq.br/2771884202728444
dc.contributor.refereeLima, Joel
dc.contributor.refereeSouza, Tânia Nogueira Fonseca
dc.date.accessioned2025-04-09T15:20:29Z
dc.date.available2025-04-09T15:20:29Z
dc.date.issued2020-02-21
dc.description.abstractOs ferros fundidos são ligas ferro-carbono que apresentam uma combinação de propriedades físicas e mecânicas atrativas para inúmeras aplicações na indústria em geral. Nodulares ou dúcteis apresentam, em sua microestrutura, a grafita na forma esferoidal e constituem uma importante família dos ferros fundidos. Devido à sua tenacidade, ductilidade e resistência mecânica são empregados em exigentes aplicações de setores como a indústria automotiva e de geração de energia eólica. Uma particularidade destas ligas é a soldabilidade, que sempre foi vista como complexa e de difícil execução se comparada à soldagem dos aços. Tal dificuldade está intimamente ligada ao seu elevado teor de carbono. Contudo, a soldagem traz também benefícios, podendo ser aplicada na união ou em reparos de defeitos de fabricação ou de danos em uso. Dessa forma, o objetivo dessa pesquisa foi estudar o efeito das temperaturas de pré e pós-aquecimento de soldagem sobre as características microestruturais e mecânicas da zona termicamente afetada em ferro fundido nodular. Em relação aos testes com pré-aquecimento apenas, para um aumento da temperatura observou-se um aumento da largura e penetração do cordão, da área da seção transversal da zona fundida, bem como da largura da zona termicamente afetada, enquanto o ensaio por líquido penetrante revelou diminuição das descontinuidades. Os valores de microdureza para a zona termicamente afetada tenderam a diminuir à medida que se aproximou do metal de base. Além disso, estes valores foram mais próximos entre si quanto maior foi a temperatura de préaquecimento, formando martensita e austenita retida. Após tratamento térmico de recozimento, a zona termicamente afetada apresentou valores de dureza similares aos do metal de base, formando microestruturas características do mesmo (perlita,ferrita e grafita nodular).
dc.description.abstractotherCast irons are ferro-carbon alloys that have a combination of attractive physical and mechanical properties for countless general industry applications. Nodular or ductile, they present, in the microstructure, graphite in spheroidal form and constitute an important family of cast irons. Due to its toughness, ductility and mechanical resistance, they are used in demanding applications in sectors such as the automotive and wind power generation industry. A particularity of these alloys is the weldability, which has always been seen as complex and difficult to perform when compared to steel welding. This difficulty is closely linked to the high carbon content. However, welding also has benefits, and it can be applied on joining or manufacturing defects or damage in use repairing. Thus, the objective of this research was to study the effect of pre and post-heating temperatures on the microstructural and mechanical characteristics of the heat-affected zone in nodular cast iron. Related to tests with preheating, for a temperature increment, an increasing in the width and penetration of the weld bead was observed, in the transversal section area of the molten zone, as well as in the width of the heat-affected zone, while the liquid penetrant test revealed discontinuities reduction. The heat-affected zone hardness values decreases from the molten to the base metal. In addition, these values were closer to each for higher preheating temperature, forming martensite and retained austenite. After annealing heat treatment, the heat-affected zone showed hardness values similar to those of the base metal, forming microstructures characteristic of the same (perlite, ferrite and nodular graphite).
dc.description.sponsorshipFinanciadora de Estudos e Projetos (FINEP) Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.identifier.urihttps://repositorio.cefetmg.br//handle/123456789/1157
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia de Materiais
dc.subjectSoldagem
dc.subjectFerro fundido nodular
dc.subjectTratamento térmico
dc.subjectMicroestrutura - Metalografia
dc.titleInfluência das temperaturas de pré e pós-aquecimento de soldagem sobre as características microestruturais e mecânicas da zona termicamente afetada em ferro fundido nodular
dc.typeDissertação

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Influência das temperaturas de pré e pós-aquecimento de soldagem sobre as características microestruturais e mecânicas da zona termicamente afetada em ferro fundido nodular.pdf
Tamanho:
7.28 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.39 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia de Materiais