Estudo da mitigação de retração livre e com restrição em argamassas de escória de alto forno álcali-ativadas

Página do item simplificado
dc.contributor.advisorBorges, Paulo Henrique Ribeiro
dc.contributor.advisorLatteshttp://lattes.cnpq.br/5399317473703342
dc.contributor.authorFragoso, Vanessa Serbate Borges
dc.contributor.referee1Paulo Henrique Ribeiro Borges
dc.date.accessioned2023-06-16T15:27:51Z
dc.date.available2023-06-16T15:27:51Z
dc.date.issued2021
dc.description.abstractA escória de alto forno granulada alcalinamente ativada é uma opção tecnológica e sustentável com promissora utilização como argamassa de reparo estrutural. Entretanto, argamassas produzidas a partir deste material apresentam elevada retração, quando comparadas com argamassas de cimento Portland. O uso de precursores reagentes de materiais expansivos ou com taxa de retração menor que a escória, são potenciais mitigadores para a retração. Neste trabalho, óxido de magnésio, sulfato de cálcio e cimento Portland em percentuais entre 5 e 25% foram substituintes da escória de alto forno, em 10 diferentes formulações de argamassa álcali-ativada. As argamassas foram caracterizadas por difração de raios X, calorimetria isotérmica, ensaio de resistência à compressão, absorção de água, retração livre e retração com restrição. A microestrutura foi avaliada por microscopia eletrônica de varredura (MEV). Os resultados numéricos foram submetidos ao método de análise de variância, com delineamento inteiramente casualizado e teste de Tukey a um nível de significância de 5%, utilizando o software SISVAR. Os resultados apontaram para uma redução média de 60% na retração livre das formulações com cimento Portland aos 7 dias e de 30% a partir dos 28 dias, com qualquer percentual de substituição. A substituição por sulfato de cálcio ocasionou reações preferenciais com a solução alcalina e consequente queda do desempenho mecânico das formulações. Ainda assim, para substituição de 5% foi verificada redução da retração livre em 36% aos 28 dias. O óxido de magnésio apresentou pouca dispersão na pasta, agindo como filler e nenhuma alteração na retração foi constatada. Nenhuma das formulações alterou a densidade de fissuras das argamassas na retração com restrição.
dc.description.abstractotherAlkaline activated granulated blast furnace slag is a technological and sustainable option with promising use as a structural repair mortar. However, mortars produced from this material show high shrinkage when compared to Portland cement mortars. Reactive precursors of expansive materials or a shrinkage rate lower than of slag are potential shrinkage mitigators. In this work, magnesium oxide, calcium sulfate and Portland cement in percentages between 5 and 25% were substitutes for blast furnace slag, in 10 different alkali-activated mortar formulations. The mortars were characterized by X-ray diffraction, isothermal calorimetry, compressive strength, water absorption, free shrinkage and restricted shrinkage. In addition, the microstructure was evaluated by scanning electron microscopy (SEM). The numerical results were subjected to the analysis of variance method, with a completely randomized design and Tukey test at a significance level of 5%, using the SISVAR software. The results pointed to an average reduction of 60% in the free shrinkage of formulations with Portland cement at 7 days and 30% after 28 days, with any percentage of replacement. The substitution for calcium sulfate caused preferential reactions with the alkaline solution and a consequent decrease in the mechanical performance of the formulations. Even so, for 5% substitution there was a 36% reduction in free shrinkage at 28 days. Magnesium oxide showed little dispersion in the paste, acting as a filler and no change in shrinkage was found. None of the formulations changed the crack density of mortars in shrinkage with restriction.
dc.identifier.urihttps://repositorio.cefetmg.br/handle/123456789/289
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia Civil
dc.subjectMateriais de construção
dc.subjectArgamassas - Manutenção e reparos
dc.subjectAditivos
dc.subjectMateriais compostos
dc.subjectResistência de materiais
dc.titleEstudo da mitigação de retração livre e com restrição em argamassas de escória de alto forno álcali-ativadas
dc.typeThesis
dspace.entity.type

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Estudo da mitigacao de retracao livre e com restricao em argamassas de escoria de alto forno alcali-ativadas_Dissertacao.pdf
Tamanho:
5.71 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.71 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia Civil