Avaliação da microestrutura e das propriedades mecânicas do ferro fundido nodular resultante de variações no percentual de nodularizante fabricado pelo processo in mold

Página do item simplificado
dc.contributor.advisorCorrêa, Elaine Carballo Siqueira
dc.contributor.advisor-coSantos, Cláudio Lúcio Pereira
dc.contributor.advisor-coLatteshttp://lattes.cnpq.br/1397432709823824
dc.contributor.advisorLatteshttp://lattes.cnpq.br/3203046752707862
dc.contributor.authorDuarte, Thallita Steffane
dc.contributor.authorLatteshttp://lattes.cnpq.br/7906423532521593
dc.contributor.refereeCorrêa, Elaine Carballo Siqueira
dc.contributor.refereeSantos, Cláudio Lúcio Pereira
dc.contributor.refereeLopes, Wellington
dc.contributor.refereeTrajano, Adriano Amâncio
dc.date.accessioned2026-09-29T18:11:12Z
dc.date.available2026-09-29T18:11:12Z
dc.date.issued2026-06-18
dc.description.abstractEste trabalho apresenta a avaliação da microestrutura e das propriedades mecânicas do ferro fundido nodular produzido pelo processo in mold, investigando a influência da variação dopercentual de liga nodularizante à base de FeSiMg com lantânio na formação da grafita e no comportamento mecânico do material. Foram analisadas e correlacionadas a morfologia da grafita, a nodularidade, a fração de grafita, a quantidade de partículas nodulares e as propriedades mecânicas obtidas, como resistência mecânica, ductilidade e dureza Brinell. A realização da parte experimental iniciou-se com a fabricação do material pelo processo de fundição, utilizando diferentes quantidades de liga nodularizante aplicadas ao processo de nodularização in mold. Durante o processo, os parâmetros metalúrgicos e químicos foram monitorados desde a preparação do metal até o vazamento das peças. Posteriormente, foram realizadas análises químicas, metalográficas e mecânicas, incluindo microscopia óptica, contagem de nódulos, ensaio de tração e ensaio de dureza Brinell. Os resultados demonstraram que as amostras com maiores percentuais de nodularizante apresentaram elevada nodularidade, predominância de grafita esferoidal e melhores propriedades mecânicas. Em contrapartida, a redução da quantidade de liga nodularizante favoreceu a formação de grafita degenerada e ocasionou queda significativa da resistência mecânica e da ductilidade do material. Dessa forma, verificou-se a forte influência do processo de nodularização sobre a microestrutura e o desempenho mecânico do ferro fundido nodular.
dc.description.abstractotherThis work presents the evaluation of the microstructure and mechanical properties of nodular cast iron produced by the in mold process, investigating the influence of variations in the percentage of FeSiMg-based nodularizing alloy with lanthanum on graphite formation and on the mechanical behavior of the material. Graphite morphology, nodularity, graphite fraction, quantity of nodular particles, and the obtained mechanical properties, such as tensile strength, yield strength, elongation, and hardness, were analyzed and correlated. The experimental procedure began with the production of the material through the casting process, using different amounts of nodularizing alloy applied in the in mold nodularization process. During the process, metallurgical and chemical parameters were monitored from metal preparation to mold pouring. Subsequently, chemical, metallographic, and mechanical analyses were performed, including optical microscopy, nodule counting, tensile testing, and Brinell hardness testing. The results demonstrated that the samples with higher percentages of nodularizing alloy presented high nodularity, predominance of spheroidal graphite, and better mechanical properties. In contrast, the reduction in the amount of nodularizing alloy favored the formation of degenerated graphite and caused a significant decrease in the mechanical strength and ductility of the material. Therefore, a strong influence of the nodularization process on the microstructure and mechanical performance of nodular cast iron was verified.
dc.identifier.urihttps://repositorio.cefetmg.br//handle/123456789/3067
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.departmentDepartamento de Engenharia de Materiais
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia de Materiais
dc.subjectFerro Fundido Nodular - Propriedades mecânicas
dc.subjectMicroestrutura
dc.subjectGrafita
dc.titleAvaliação da microestrutura e das propriedades mecânicas do ferro fundido nodular resultante de variações no percentual de nodularizante fabricado pelo processo in mold
dc.typeTrabalho de Conclusão de Curso da Graduação

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Avaliação da microestrutura e das propriedades mecânicas do ferro fundido nodular resultante de variações no percentual de nodularizante fabricado pelo processo in mold.pdf
Tamanho:
13.53 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.39 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Engenharia de Materiais (Belo Horizonte - Nova Suiça)