Influência do tipo e de parâmetros de tratamento intercrítico na microestrutura e no comportamento mecânico de aços bifásicos
| dc.contributor.advisor | Corrêa, Elaine Carballo Siqueira | |
| dc.contributor.advisor-co | Lopes, Wellington | |
| dc.contributor.advisor-coLattes | http://lattes.cnpq.br/4445376135095677 | |
| dc.contributor.advisorLattes | http://lattes.cnpq.br/3203046752707862 | |
| dc.contributor.author | Silva, Nayara Aparecida Neres da | |
| dc.contributor.authorLattes | http://lattes.cnpq.br/8229230713584828 | |
| dc.contributor.referee | Silva, Leonardo Roberto da | |
| dc.contributor.referee | Aguilar, Maria Teresa Paulino | |
| dc.contributor.referee | Santos, Leandro de Arruda | |
| dc.date.accessioned | 2025-03-26T16:13:29Z | |
| dc.date.available | 2025-03-26T16:13:29Z | |
| dc.date.issued | 2017-03-07 | |
| dc.description.abstract | Os aços bifásicos ou dual phase (DP) surgiram como uma solução alternativa com grandes vantagens aos aços convencionais, pois combinam alta resistência mecânica e boa conformabilidade. As propriedades mecânicas desses aços estão diretamente relacionadas às suas características microestruturais: tipo, quantidade, morfologia e distribuição dos constituintes, que, por sua vez, dentre outros aspectos, dependem dos parâmetros de processamento utilizados, principalmente do tipo de tratamento térmico realizado. Nesta pesquisa, foi avaliada a influência dos tratamentos intercríticos direto e contínuo, do tempo de encharque e da temperatura de recozimento na microestrutura e no comportamento mecânico de aços bifásicos. Análises da microestrutura após os tratamentos térmicos de recozimento intercrítico direto e contínuo foram realizadas por microscopia óptica (MO) e microscopia eletrônica de varredura (MEV). A caracterização mecânica foi conduzida por ensaios de dureza, tração e ultramicrodureza. Análises sobre o encruamento do material foram realizadas com o auxílio das abordagens: método de linearização da curva ? x ?, taxa de encruamento, expoente de encruamento instantâneo e análise de Crussard-Jaoul. Avaliações do comportamento a deformação na tração em diferentes magnitudes também foram realizadas com o auxílio da penetração instrumentada e MEV. Finalmente, foi verificado que a microestrutura e as propriedades mecânicas das amostras tratadas por recozimento intercrítico direto foram mais influenciadas pelos efeitos do tempo e da temperatura intercrítica. Em geral, elevados valores de dureza na interface ferrita/martensita foram observados. A análise de Crussard-Jaoul mostrou-se mais completa para a análise do encruamento. Palavras-chave: Aços bifásicos, tratamento térmico intercrítico, microestrutura, propriedades mecânicas. | |
| dc.description.abstractother | Dual phase steels (DP) have emerged as an alternative solution with great advantages to conventional steels, as they combine high mechanical strength and good formability. The mechanical properties of these steels are directly related to their microstructural characteristics: type, amount, morphology and distribution of the constituents, which depend on the processing parameters, especially the type of heat treatment performed. In this research, the influence of direct and continuous intercritical annealing, the holding time and annealing temperature in the microstructure and on mechanical behaviour in dual phase steels were evaluated. Analysis about the microstructure after direct and continuous intercritical annealing were performed by optical microscopy (OM) and scanning electron microscopy (SEM). The Mechanical characterization was conducted by hardness, tensile and microhardness tests. Work hardening evaluations of the material was performed using the following approaches: linearization method of the curve ? x ?, work hardening rate, instantaneous work hardening index and Crussard-Jaoul analysis. Tensile deformation behaviour analysis in different magnitudes were also performed with the aid of instrumented penetration and SEM. Finally, it was verified that the microstructure and the mechanical properties of the samples treated by direct intercritical annealing were more influenced by the effects of holding time and the intercritical temperature. In general, high hardness values at the ferrite / martensite interface were observed. Crussard-Jaoul analysis proved to be more complete for work hardening analysis. Keywords: Dual phase steels, intercritical annealing, microstructure, mechanical properties. | |
| dc.identifier.uri | https://repositorio.cefetmg.br//handle/123456789/967 | |
| dc.language.iso | pt | |
| dc.publisher | Centro Federal de Educação Tecnológica de Minas Gerais | |
| dc.publisher.country | Brasil | |
| dc.publisher.department | Departamento de Engenharia de Materiais | |
| dc.publisher.initials | CEFET-MG | |
| dc.publisher.program | Programa de Pós-Graduação em Engenharia de Materiais | |
| dc.subject | Aço | |
| dc.subject | Tratamento térmico | |
| dc.subject | Microestrutura | |
| dc.subject | Metais - Propriedades mecânicas | |
| dc.title | Influência do tipo e de parâmetros de tratamento intercrítico na microestrutura e no comportamento mecânico de aços bifásicos | |
| dc.type | Dissertação |
Arquivos
Pacote Original
1 - 1 de 1
Carregando...
- Nome:
- Influência do tipo e de parâmetros de tratamento intercrítico na microestrutura e no comportamento mecânico de aços bifásicos.pdf
- Tamanho:
- 10.2 MB
- Formato:
- Adobe Portable Document Format
Licença do Pacote
1 - 1 de 1
Nenhuma Miniatura disponível
- Nome:
- license.txt
- Tamanho:
- 1.39 KB
- Formato:
- Item-specific license agreed to upon submission
- Descrição: