Estudo da resistência à corrosão do aço ASTM 304 e 439, em solução de 3,5% de NACL com diferentes níveis de redução de espessura no processo de laminação a frio

Página do item simplificado
dc.contributor.advisorDumont, Marcello Rosa
dc.contributor.advisorLatteshttp://lattes.cnpq.br/5092556253652672
dc.contributor.authorRezende, Isabella Teixeira
dc.contributor.authorLatteshttp://lattes.cnpq.br/7266479163618811
dc.contributor.refereeDumont, Marcello Rosa
dc.contributor.refereeCorrêa, Elaine Carballo Siqueira
dc.contributor.refereeLabiapari, Wilian da Silva
dc.date.accessioned2025-03-17T19:33:25Z
dc.date.available2025-03-17T19:33:25Z
dc.date.issued2022-07-05
dc.description.abstractOs aços inoxidáveis são aços comerciais bastante utilizados devido à sua alta resistência à corrosão e propriedades mecânicas. Diversos estudos têm demostrado que o trabalho a frio em aços inoxidáveis induz a transformação da austenita em martensita e assim provocaram alterações na resistência à corrosão. Neste trabalho foram utilizadas amostras de aço inoxidável ASTM AISI 304 e ASTM AISI 439 com 3 mm de espessura. As chapas foram conformadas por laminação a frio, sem recozimento, com redução final de espessura de 10% até 50%. As amostras foram caracterizadas por meio de ensaio de microdureza Vickers, ensaio metalográfico, difração de raios-x e polarização potenciodinâmica em solução de NaCl 3,5%. A formação da fase martensita a' induzida pela deformação foi observada nas amostras AISI 304, acompanhado pelo aumento da dureza, que aumentaram à medida que trabalho a fio aumentou. Para o AISI 439 apenas a fase ferrita foi observada, com possível formação de carbonetos. Nos ensaios de polarização potenciodinâmica foi percebida uma variação na resistência a corrosão das amostras analisadas à medida que a deformação a frio aumentou, mas apresentando uma resistência a corrosão similar em todos as amostras. A formação da martensita nessas condições de deformação impostas não gerou variação nos parâmetros eletroquímicos estudados. Por outro lado, uma menor densidade de corrente foi requerida na formação da camada passiva, sugerindo uma maior resistência à corrosão nas amostras menos deformadas. Comparativamente o AISI 304 e o AISI 439 tal como recebido e com redução de 50% de espessura, o AISI 304 apresentou uma resistência a corrosão superior que o AISI 439.
dc.description.abstractotherStainless steel are commercial steels widely used due to their high corrosion resistance and mechanical properties. Several studies have been demonstrated the deformation- induced transformation of martensite on stainless steels and thus cause changes on the corrosion resistance. On this work samples of ASTM AISI 304 and ASTM AISI 439 stainless steel of 3 mm of thickness were used. The plates were formed by cold-rolling, without annealing, with a thickness reduction from 10% to 50%. The samples were characterized by Vickers micro-hardness, metallographic test, X-ray diffraction and potentiodynamic polarization under 3.5% NaCl solution. The deformation-induced transformation of ?'-martensite was observed on AISI 304 samples, followed by hardness increase, in function of thickness reduction. For AISI 439 samples only ferrite phase was observed with probable precipitation of carbides. In the potentiodynamic polarization tests, a variation in the corrosion resistance of AISI 304 was noticed as the cold deformation increased, but presenting a similar corrosion resistance in all samples. The formation of martensite under these imposed strain conditions did not generate variation in the electrochemical parameters studied. On the other hand, a lower current density was required in the passive layer formation, suggesting a greater resistance to corrosion in the less deformed samples. Compared to AISI 304 and AISI 439 as- received and with a 50% of thickness reduction, AISI 304 showed a superior corrosion resistance than AISI 439.
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior – Brasil (CAPES) – Código de Financiamento 001
dc.identifier.urihttps://repositorio.cefetmg.br//handle/123456789/817
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia de Materiais
dc.subjectAço inoxidável
dc.subjectLaminação a frio
dc.subjectCorrosão
dc.titleEstudo da resistência à corrosão do aço ASTM 304 e 439, em solução de 3,5% de NACL com diferentes níveis de redução de espessura no processo de laminação a frio
dc.typeDissertação

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Estudo da resistência à corrosão do aço ASTM 304 e 439, em solução de 3,5% de NACL com diferentes níveis de redução de espessura no processo de laminação a frio.pdf
Tamanho:
1.91 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.39 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia de Materiais