O Repositório será lançado oficialmente no dia 9 de abril de 2025 às 14h30min no miniauditório do Campus Nova Suiça.
 

Influência do processamento térmico no desenvolvimento da microestrutura multiconstituída e no comportamento mecânico de um aço assistido pelo efeito TRIP

Página do item simplificado
dc.contributor.advisorCorrêa, Elaine Carballo Siqueira
dc.contributor.advisor-coLopes, Wellington
dc.contributor.advisor-coLatteshttp://lattes.cnpq.br/4445376135095677
dc.contributor.advisorLatteshttp://lattes.cnpq.br/3203046752707862
dc.contributor.authorBraga, Cintia
dc.contributor.authorLatteshttp://lattes.cnpq.br/3081854375300335
dc.contributor.refereeMaia, Nilton da Silva
dc.contributor.refereeSantos, Dagoberto Brandão
dc.contributor.refereeSilva, Gilmar Cordeiro da
dc.date.accessioned2025-03-24T15:56:27Z
dc.date.available2025-03-24T15:56:27Z
dc.date.issued2018-02-20
dc.description.abstractOs aços assistidos pelo efeito TRIP apresentam grande potencial e aplicabilidade na indústria automobilística devido às suas combinações ótimas de propriedades, que permitem a produção de chapas mais finas sem o comprometimento do desempenho dos componentes. A excelente combinação de alta resistência mecânica, ductilidade e elevada resistência ao impacto observada nos aços TRIP se deve a estrutura multifásica presente nestes aços, produzida em geral por um processamento térmico que consiste em um aquecimento intercrítico seguido de tratamento isotérmico na faixa de transformação bainítica. Neste trabalho foram analisados os efeitos das temperaturas de recozimento intercrítico e de transformação bainítica, bem como do tempo de tratamento isotérmico, na microestrutura e propriedades mecânicas de um aço assistido pelo efeito TRIP. As análises foram conduzidas em termos de microscopia óptica, microscopia eletrônica de varredura, microscopia de força atômica, difração de raios-X, ensaios de dureza, ensaios de tração e análises referentes ao comportamento de encruamento do material por quatro métodos distintos: linearização da curva σ x ε, taxa de encruamento, expoente de encruamento instantâneo e análise de Crussard-Jaoul. O aumento do tempo de austêmpera favoreceu a formação de bainita com morfologia em ripas e permitiu maior retenção de austenita no material, resultando em menores valores de dureza e limite de escoamento. A redução na temperatura de austêmpera favoreceu o refinamento da estrutura bainítica e resultou em frações de austenita retida inferiores, porém com maior teor de carbono. Em geral, a utilização de uma menor temperatura intercrítica promoveu menores valores de dureza devido ao aumento da fração volumétrica de ferrita. Quanto aos métodos de encruamento utilizados, a análise pelo expoente de encruamento instantâneo apresentou-se como a mais adequada para a avaliação do comportamento de deformação do aço estudado.
dc.description.abstractotherTRIP-assisted steels shows great potential and applicability in automotive industry due to their excellent combinations of properties that allow the production of thinner sheets without compromising the performance of components. The excellent combination of high strength, ductility and crashworthiness observed in TRIP steels is related to the multiphase structure present in these steels, produced usually by a thermal treatment consisting in intercritical annealing followed by isothermal treatment in the bainitic transformation range. In this work the effects of the intercritical annealing and bainitic transformation temperatures, as well as the holding time at isothermal bainitic temperature, on the microstructure and mechanical properties of a TRIP-assisted steel were analyzed. Evaluations were conducted in terms of optical microscopy, scanning electron microscopy, atomic force microscopy, X-ray diffraction, hardness tests, tensile tests and analyzes concerning the work hardening behavior of the material by four different methods: Hollomon analysis, work hardening rate, instantaneous n value and Crussard-Jaoul analysis. Higher austempering times favored the formation of bainite with lath morphology and allowed greater retention of austenite, resulting in lower hardness values and yield strength. Reduction of austempering temperature favored the refinement of the bainitic structure and resulted in lower retained austenite fractions, but with a higher carbon content. In general, the use of a lower intercritical temperature promoted lower hardness values due to the increase of ferrite proportion. As for the hardening methods used, the analysis concerning the instantaneous n value was the most adequate for the deformation behavior evaluation of the studied steel.
dc.identifier.urihttps://repositorio.cefetmg.br//handle/123456789/908
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.departmentDepartamento de Engenharia de Materiais
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia de Materiais
dc.subjectAço - Tratamento térmico
dc.subjectAço bainita
dc.subjectAustenita
dc.titleInfluência do processamento térmico no desenvolvimento da microestrutura multiconstituída e no comportamento mecânico de um aço assistido pelo efeito TRIP
dc.typeDissertação

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Influência do processamento térmico no desenvolvimento da microestrutura multiconstituída e no comportamento mecânico de um aço assistido pelo efeito TRIP.pdf
Tamanho:
118.15 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.39 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia de Materiais