Influência da temperatura do tratamento térmico de revenimento de duplo estágio sobre a microestrutura e propriedades de metal de solda 13%Cr, 4%Ni e 0,4%Mo

Página do item simplificado
dc.contributor.advisorVaz, Cláudio Turani
dc.contributor.advisorLatteshttp://lattes.cnpq.br/5386844601893935
dc.contributor.authorVilela, Keila Cristina
dc.contributor.authorLatteshttp://lattes.cnpq.br/0601511674160806
dc.contributor.refereeCorrêa, Elaine Carballo Siqueira
dc.contributor.refereeLiberato, Frank de Mello
dc.date.accessioned2025-04-09T16:15:52Z
dc.date.available2025-04-09T16:15:52Z
dc.date.issued2020-02-27
dc.description.abstractO aço inoxidável martensítico fundido CA6NM é empregado na construção de rotores, componentes utilizados em turbinas hidráulicos. Sua escolha é devido ao custo de fabricação e ao desempenho em operação. Na fabricação ou reparo desses rotores é empregado um metal de solda similar, contendo 13% de cromo, 4% de níquel e 0,4% de molibdênio, com teores de carbono inferiores a 0,04%. Por meio do emprego do tratamento térmico de revenimento de duplo estágio, é possível obter maiores valores de tenacidade. O objetivo deste estudo foi avaliar o efeito da temperatura sobre a microestrutura e tenacidade deste metal de solda, analisado em cinco diferentes condições, além de como soldado. As microestruturas foram analisadas por meio da Microscopia Óptica (MO) e Microscopia Eletrônica de Varredura (MEV). A quantidade de austenita retida foi obtida por meio da realização da Difração de Raios-X (DRX). Foi realizada a caracterização mecânica do metal de solda, com a realização do ensaio Charpy com entalhe em V, para obtenção da tenacidade, e do ensaio de dureza Vickers. Em todas as condições analisadas formou-se austenita retida, porém, os maiores teores foram encontrados nos tratamentos térmicos de duplo estágio. O revenimento realizado a 580°C/2h foi o que levou à obtenção de menor fração de austenita retida, enquanto a 650°C/2h+580°C/4h foi obtido o maior teor desse constituinte. O valor da tenacidade do metal de solda apresentou relação diretamente proporcional à porcentagem de austenita retida encontrada. Já para a dureza, essa relação foi inversa. Em todas as condições analisadas, o material apresentou mais característica de fratura frágil. As melhores propriedades mecânicas, de acordo com o objetivo do presente estudo, foram encontradas no tratamento térmico de duplo estágio.
dc.description.abstractotherCA6NM cast martensitic stainless steel is used in the construction of rotors, components used in hydraulic turbines. Your choice is due to manufacturing cost and operating performance. A similar weld metal, containing 13% chromium, 4% nickel and 0,4% molybdenum, with carbon contents below 0,04% is used in the manufacture or repair of these rotors,. Through the use of double-stage tempering heat treatment, it is possible to obtain higher values of toughness. The aim of this study was to evaluate the effect of temperature on the microstructure and toughness of this weld metal, analyzed under five different conditions, in addition to as welded. The microstructures were analyzed using Optical Microscopy (MO) and Scanning Electron Microscopy (SEM). The amount of austenite retained was obtained by performing X-Ray Diffraction (XRD). The mechanical characterization of the weld metal was carried out, with the performance of the V-notch Charpy test, to obtain the toughness, and the Vickers hardness test. In all conditions analyzed, retained austenite was formed, however, the highest levels were found in double-stage heat treatments. The tempering carried out at 580°C/2h was what led to the obtaining of the lowest fraction of retained austenite, while at 650°C/2h + 580°C/4h the highest content of this constituent was obtained. The toughness value of the weld metal was directly proportional to the percentage of retained austenite found. As for hardness, this relationship was reversed. In all the analyzed conditions, the material presented more characteristic of fragile fracture. The best mechanical properties, according to the objective of the present study, were found in the double stage heat treatment.
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) Centro Federal de Educação Tecnológica de Minas Gerais (CEFET-MG)
dc.identifier.urihttps://repositorio.cefetmg.br//handle/123456789/1158
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia de Materiais
dc.subjectAço inoxidável martensítico
dc.subjectSolda e soldagem
dc.subjectAustenita
dc.subjectTenacidade dos materiais
dc.titleInfluência da temperatura do tratamento térmico de revenimento de duplo estágio sobre a microestrutura e propriedades de metal de solda 13%Cr, 4%Ni e 0,4%Mo
dc.typeDissertação

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Influência da temperatura do tratamento térmico de revenimento de duplo estágio sobre a microestrutura e propriedades de metal de solda.pdf
Tamanho:
3.48 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.39 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia de Materiais