Propriedades mecânicas e de durabilidade de argamassas de reparo com agregado reciclado e adição de óxido de grafeno
dc.contributor.advisor | Poggiali, Flávia Spitale Jacques | |
dc.contributor.advisorLattes | http://lattes.cnpq.br/6824739413179983 | |
dc.contributor.author | Santos, Janaíne Conceição | |
dc.contributor.referee1 | Flávia Spitale Jacques Poggiali | |
dc.contributor.referee2 | Péter Ludvig | |
dc.contributor.referee3 | José Márcio Fonseca Calixto | |
dc.contributor.referee4 | Luiz Orlando Ladeira | |
dc.date.accessioned | 2023-06-19T12:37:29Z | |
dc.date.available | 2023-06-19T12:37:29Z | |
dc.date.issued | 2022-12-19 | |
dc.description.abstract | Os resíduos da construção contribuem significativamente para a poluição do meio ambiente. A construção civil busca por inovações que aumentem o desempenho de seus materiais, reduzam seus custos e garantam sua sustentabilidade. As argamassas são um tipo de compósito cimentício comumente utilizado para assentamento de tijolos, placas cerâmicas, revestimentos e reparos em estruturas. O uso de agregado miúdo reciclado no traço de argamassas tem se mostrado uma alternativa para a destinação dos resíduos de construção e demolição. No entanto, a substituição do agregado natural por agregados de RCD compromete as resistências à compressão, tração e flexão, bem como a durabilidade da argamassa. Nesse sentido, a incorporação de pequenas quantidades de óxido de grafeno (OG) em argamassas teria o potencial de melhorar suas propriedades mecânicas e de durabilidade. O presente trabalho propôs a avaliação das propriedades mecânicas e de durabilidade de argamassas confeccionadas com substituição de 100% dos agregados naturais pelos agregados de resíduos de construção e demolição (RCD), e adição de óxido de grafeno em dois teores de 0,05% e 0,10% (da massa de cimento). As argamassas foram confeccionadas em quatro traços: com agregado natural, com agregado de RCD, com agregado de RCD e adição de 0,05% de OG e com agregado de RCD e adição de 0,1% de OG. Os ensaios realizados abrangeram a resistência à compressão, resistência à tração na flexão, módulo de elasticidade, absorção de água e carbonatação. Os resultados dos ensaios indicam que a substituição do agregado natural por agregado de RCD mais adição de OG em argamassas de reparo resultaram no aumento da resistência à compressão (21%), da resistência à tração na flexão (10%), do módulo de elasticidade (6%) e na diminuição da absorção de água (7%) comparada à argamassa de RCD. Porém, houve um aumento na frente de carbonatação (14%), visto que a argamassa R já havia apresentado menor frente de carbonatação do que a argamassa N. | |
dc.description.abstractother | In the last few decades, the construction sector has experienced intense development, culminating in large amounts of waste, especially derived from demolition and construction activities. The construction industry is continuously searching for innovations, performance gain, cost reduction, and sustainability. The use of the recycled fine aggregate, made from construction and demolition waste, has proved to be an alternative for incorporated in the composition of the mortar. However, the replacement of natural aggregate by RCD aggregates, as long as the mechanical strength and durability of the mortar decrease issue was solved. In this sense, small additions of graphene oxide (GO) could have the potential to improve the mechanical performance and durability of mortars. The improvement of the mechanical properties and durability could encourage the construction industry to use, furthermore would support to reduce the depletion of available natural resources. This work evaluates the mechanical and durability properties of mortars, made up of 100% of replacement of the natural aggregates to recycled aggregates, and graphene oxide added in two levels of 0.05% and 0.10% (of the cement mass). The mortars were made in four types: natural aggregate, RCD aggregate, RCD aggregate an addition of 0.05% of OG and RCD aggregate an addition of 0.1% of OG. The tests carried out covered the compressive strength, flexural tensile strength, modulus of elasticity, water absorption and carbonation. The results of the tests indicate that the replacement of natural aggregate by RCD aggregate plus the addition of OG in repair mortars resulted in an increase in compressive strength (21%), flexural tensile strength (10%), modulus of elasticity (6%) and decrease in the water absorption (7%) compared to RCD mortar. However, there was an increase in the carbonation front (14%), since the mortar R had already obtainable a smaller carbonation than mortar N. | |
dc.identifier.uri | https://repositorio.cefetmg.br/handle/123456789/296 | |
dc.language.iso | pt | |
dc.publisher | Centro Federal de Educação Tecnológica de Minas Gerais | |
dc.publisher.country | Brasil | |
dc.publisher.initials | CEFET-MG | |
dc.publisher.program | Programa de Pós-Graduação em Engenharia Civil | |
dc.subject | Argamassa - Propriedades mecânicas | |
dc.subject | Resíduos de demolição e construção | |
dc.subject | Materiais de construção - Vida útil | |
dc.subject | Materiais compostos | |
dc.title | Propriedades mecânicas e de durabilidade de argamassas de reparo com agregado reciclado e adição de óxido de grafeno | |
dc.type | Thesis | |
dspace.entity.type |
Arquivos
Pacote Original
1 - 1 de 1
Carregando...
- Nome:
- Propriedades mecanicas e de durabilidade de argamassas de reparo com agregado reciclado e adicao de oxido de grafeno_Dissertacao.pdf
- Tamanho:
- 2.41 MB
- Formato:
- Adobe Portable Document Format
Licença do Pacote
1 - 1 de 1
Nenhuma Miniatura disponível
- Nome:
- license.txt
- Tamanho:
- 1.71 KB
- Formato:
- Item-specific license agreed to upon submission
- Descrição: