Estudo do comportamento do cavaco durante a furação da liga AL-MG-SI 6061-T6 utilizando ferramentas de aço rápido sem e com revestimento de DLC

Página do item simplificado
dc.contributor.advisorSantos, Sandro Cardoso
dc.contributor.advisor-coMartins, Paulo Sérgio
dc.contributor.advisor-coLatteshttp://lattes.cnpq.br/6979394011332346
dc.contributor.advisorLatteshttp://lattes.cnpq.br/6898188197618037
dc.contributor.authorPereira, Luiza Amelia de Melo
dc.contributor.authorLatteshttp://lattes.cnpq.br/0251845050693343
dc.contributor.refereeSantos, Sandro Cardoso
dc.contributor.refereeMartins, Paulo Sérgio
dc.contributor.refereeMottin, Arthur Caron
dc.contributor.refereeFernandes, Gustavo Henrique Nazareno
dc.contributor.refereePereira, Mayara Fernanda
dc.date.accessioned2025-11-17T11:36:21Z
dc.date.available2025-11-17T11:36:21Z
dc.date.issued2025-07-31
dc.description.abstractAs ligas da classe Al-Mg-Si 6061-T6 vêm sendo aplicadas em várias áreas da indústria metal mecânica como indústria aeronáutica, automotiva, química, petroquímica e de embalagens, pois possuem excelente relação resistência-peso, boa ductilidade, baixa densidade, excelentes condutividades térmica e elétrica e resistência à corrosão. As ligas de alumínio são muito rica, mas limitando-se a investigações que levam em conta os problemas de usinagem, principalmente àqueles relacionados com forças, temperaturas, controle e formação do cavaco, e normalmente são trabalhos pontuais, em processos específicos, geralmente em apenas uma determinada liga. A formação do cavaco influencia as demais variáveis do processo de usinagem e essa formação depende muito das propriedades do material. Neste trabalho determinou-se experimentalmente as características do cavaco com foco no grau de recalque buscando avaliar o nível de deformação do cavaco sem e com o uso de DLC, além da sua relação com a microdureza, rugosidade e desvios de forma. Os revestimentos DLC não apenas reduziram o desgaste das ferramentas, mas também melhoraram a formação dos cavacos e os parâmetros de qualidade superficial. Em relação ao grau de recalque, a análise estatística indicou que os revestimentos de DLC atuaram como um lubrificante sólido durante a usinagem a seco, favorecendo o escoamento e a expulsão dos cavacos, e consequentemente, reduzindo a deformação quando comparado aos cavacos obtidos no grupo sem revestimento (G1). Já nos parâmetros microgeométricos, os valores médios de Ra foram 1,40 ± 0,31 μm para o G1, 1,43 ± 0,15 μm para o G2 e 1,26 ± 0,17 μm para o G3 e para o parâmetro Rz foram encontrados 7,69 ± 1,67 μm para o G1, 7,95 ± 0,77 μm para o G2 e 7,26 ± 0,80 μm para o G3, indicando que o Rz não sofreu influência significativa entre os grupos diferentemente de Ra. Para a assimetria e curtose, os desvios de Rsk chegaram a 212% e de Rku a 67%, e ambos não apresentaram diferenças estatisticamente significativas entre os grupos, o que pode estar relacionado à dispersão elevada dos dados.
dc.description.abstractotherThe Al-Mg-Si 6061-T6 alloy class has been widely applied in several areas of the metal-mechanical industry, such as the aerospace, automotive, chemical, petrochemical, and packaging sectors, due to its excellent strength-to-weight ratio, good ductility, low density, and outstanding thermal and electrical conductivity, as well as corrosion resistance. Although aluminum alloys have been extensively studied, most investigations focus on machining-related problems, particularly those involving forces, temperatures, chip control, and chip formation, and are usually limited to specific processes or a single alloy. Chip formation influences other machining process variables and strongly depends on the material’s properties. In this study, the chip characteristics were experimentally determined, focusing on the compression ratio to evaluate the chip deformation level with and without the use of DLC coatings, as well as its relationship with microhardness, surface roughness, and form deviations. The DLC coatings not only reduced tool wear but also improved chip formation and surface quality parameters. Regarding the chip thickness ratio, statistical analysis indicated that the DLC coatings acted as a solid lubricant during dry machining, favoring chip flow and evacuation and consequently reducing deformation compared to the uncoated group (G1). For the microgeometric parameters, the mean Ra values were 1.40 ± 0.31 μm for G1, 1.43 ± 0.15 μm for G2, and 1.26 ± 0.17 μm for G3, while the Rz values were 7.69 ± 1.67 μm for G1, 7.95 ± 0.77 μm for G2, and 7.26 ± 0.80 μm for G3, indicating that Rz was not significantly affected among the groups, unlike Ra. For skewness and kurtosis, the Rsk deviations reached 212% and Rku 67%, and both showed no statistically significant differences between the groups, which may be related to the high data dispersion.
dc.identifier.urihttps://repositorio.cefetmg.br//handle/123456789/2479
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia Mecânica
dc.subjectLigas de alumínio - Propriedades mecânicas
dc.subjectMetais - Corte
dc.subjectCaracterização de materiais
dc.titleEstudo do comportamento do cavaco durante a furação da liga AL-MG-SI 6061-T6 utilizando ferramentas de aço rápido sem e com revestimento de DLC
dc.typeDissertação

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Estudo do comportamento do cavaco durante a furação da liga AL-MG-SI 6061-T6 utilizando ferramentas de aço rápido sem e com revestimento de DLC.pdf
Tamanho:
4 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.39 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia Mecânica