Influência da adição de fluoreto como carga em shop primer a base de etil silicato de zinco sobre soldas produzidas pelo processo FCAW

Página do item simplificado
dc.contributor.advisorVaz, Cláudio Turani
dc.contributor.advisor-coSilva, Bruno Cordeiro
dc.contributor.advisor-coLatteshttp://lattes.cnpq.br/1868816663610134
dc.contributor.advisorLatteshttp://lattes.cnpq.br/5386844601893935
dc.contributor.authorRezende, Leonardo Schiavo de
dc.contributor.authorLatteshttp://lattes.cnpq.br/0629268016271602
dc.contributor.refereeVaz, Cláudio Turani
dc.contributor.refereeSilva, Bruno Cordeiro
dc.contributor.refereeCastro, Carlos Alberto Carvalho
dc.contributor.refereeFelizardo, Ivanilza
dc.date.accessioned2025-04-03T19:57:27Z
dc.date.available2025-04-03T19:57:27Z
dc.date.issued2023-10-18
dc.description.abstractIndústrias naval, offshore, de construção civil e mecânica utilizam aços estruturais que podem ficar armazenados por prolongado tempo e até expostos a intempéries. Desta forma, é necessário que esse material esteja protegido, principalmente contra corrosão. Para isso, são realizadas pinturas com uma tinta conhecida como shop primer ou tinta de pré-construção, que além de atuar como inibidor de corrosão, pode afetar negativamente o processo de soldagem e comprometer a qualidade das soldas. Para superar esses inconvenientes, é necessário desenvolver novas alternativas que produzam cordões de solda equivalentes aos obtidos em chapas sem recobrimento. Com o intuito de otimizar o processo de soldagem sobre chapas pintadas, este trabalho teve como objetivo avaliar a influência da carga de fluoreto adicionada em formulação comercial de shop primer sobre as soldas realizadas com arame tubular classe E71T1-C1A2-CS2 e proteção gasosa 100% CO2. De forma comparativa foram avaliadas quatro condições: chapa base sem primer, com primer e sem carga de fluoreto, com primer e com carga de 7,5% m/m e 15% m/m de fluoreto. Verificou-se que o primer inibe a adesão de respingos nas chapas e que influencia na morfologia da solda, gerando cordões mais largos e mais profundos. Em contrapartida, a carga de fluoreto age atenuando esses efeitos, quando comparado com os resultados obtidos com a pintura sem carga. Foi verificado também que o primer sem carga de fluoreto não altera a microestrutura em comparação com as soldas realizadas sem o seu emprego. No entanto, verificou-se que a presença de fluoreto aumenta a fração volumétrica de ferrita acicular e ferrita de segunda fase alinhada, em detrimento das reduções das frações de ferrita primária de contorno de grão e de ferrita intragranular. Por fim, os sinais elétricos coletados mostram que o primer aumenta a tensão média na soldagem e a presença do fluoreto tende a atenuar este efeito. A corrente média tende a diminuir com a presença do primer e o fluoreto intensifica esta queda. Como consequência, as amostras com carga de fluoreto apresentaram menores aportes térmicos que as demais amostras. Adicionalmente, foi observado que a presença do fluoreto influenciou a transferência metálica alterando a frequência de ciclos da tensão.
dc.description.abstractotherShipbuilding, offshore, civil construction and mechanical industries use structural steels that can be stored for a long time and even exposed to the weather. In this way the material must be protected, mainly against corrosion. For this, painting is carried out with a paint known as shop primer or pre-construction paint, which, in addition to acting as a corrosion inhibitor, can negatively affect the welding process and compromise the quality of the welds. To overcome these inconveniences, it is necessary to develop new alternatives that produce weld beads equivalent to those obtained in uncoated plates. With the aim of optimizing the welding process on plates painted with primer, this work investigated the influence of fluoride charge added in a commercial formulation of shop primer over welds made with tubular wire E71T1-C1A2-CS2 with 100% CO2 gas protection. In a comparative way, this work evaluated four conditions: base plate without primer, painted with primer without fluoride, with primer and with 7.5% m/m and 15% m/m of fluoride addition. It was verified that the primer inhibits the adhesion of the welding spatter on the plates and influences the morphology of the weld, generating wider and deeper beads. On the other hand, the fluoride acts to attenuate these effects, when compared with the results obtained with unfilled paint. It was also verified that the primer without fluoride charge does not influence the microstructures obtained in comparison with welds made without primer. However, it was found that the presence of fluoride increases the volumetric fraction of acicular ferrite and aligned second-phase ferrite reducing grain boundary primary ferrite and intragranular ferrite fractions. Finally, the electric signals shows that the primer increases the average welding voltage and the presence of fluoride tends to attenuate this effect. The average current tends to decrease with the presence of the primer and the fluoride charges intensifies this effect. Consequently, samples with fluoride load have lower thermal inputs than the other samples. Additionally, it was observed that the primer presence changes the metallic transfer increasing the voltage frequency cycles
dc.description.sponsorshipAkzo Nobel
dc.identifier.urihttps://repositorio.cefetmg.br//handle/123456789/1098
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia de Materiais
dc.subjectSoldagem por fluxo
dc.subjectArames tubulares - Soldabilidade
dc.subjectFluoretos
dc.titleInfluência da adição de fluoreto como carga em shop primer a base de etil silicato de zinco sobre soldas produzidas pelo processo FCAW
dc.typeDissertação

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Influência da adição de fluoreto como carga em shop primer a base de etil silicato de zinco sobre soldas produzidas pelo processo FCAW.pdf
Tamanho:
14.15 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.39 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia de Materiais