Análise do efeito da agitação eletromagnética sobre a evolução microestrutural, textura e propriedades magnéticas de um aço elétrico de grão não orientado com 2% de silício

Página do item simplificado
dc.contributor.advisorRocco, Daniel Leandro
dc.contributor.advisor-coPaolinelli, Sebastião da Costa
dc.contributor.advisor-coLatteshttp://lattes.cnpq.br/1342693919211133
dc.contributor.advisorLatteshttp://lattes.cnpq.br/1028283049134193
dc.contributor.authorToledo Júnior, Francisco Geraldo
dc.contributor.authorLatteshttp://lattes.cnpq.br/8812731190969725
dc.contributor.refereeMeireles, Leonel Muniz
dc.contributor.refereeLandgraf, Fernando José Gomes
dc.contributor.refereeOliveira Júnior, José Rogério de
dc.date.accessioned2025-04-30T19:20:55Z
dc.date.available2025-04-30T19:20:55Z
dc.date.issued2024-09-20
dc.description.abstractA influência do uso da agitação eletromagnética durante a solidificação no processo de lingotamento contínuo foi avaliada para um aço elétrico de grão não orientado com 2 % de silício. Amostras de bobinas laminadas a quente (BQ) oriundas de placas com agitação (46 % de grãos equiaxiais) e sem agitação (15 % de grãos equiaxiais), foram submetidas em laboratório ao recozimento inicial a 1000 °C, laminação a frio para espessura final de 0,50 mm e recozimento final em temperaturas entre 860 °C e 1100 °C. Propriedades como perda e polarização magnética foram medidas nas amostras após o recozimento final. Para avaliação da evolução microestrutural e de textura utilizou-se metalografia ótica, difratometria de raios X e EBSD (Electron Back-Scattering Diffraction). A avaliação das propriedades magnéticas foi realizada utilizando do acessório chapa única para medição de perda e polarização magnética. Em relação ao tamanho de grão da BQ e o tamanho de grão final em função do uso da agitação, os resultados se mostraram similares. Quando o recozimento da BQ foi aplicado, as amostras com o uso da agitação apresentaram crescimento preferencial de grãos. Além disso, o uso da agitação demonstrou diferenças na fração volumétrica das principais fibras (α, γ, η e θ) em todas as etapas de tratamento. Os resultados nas propriedades magnéticas, como polarização magnética (J50) e perda magnética a 1,5 T e 60 Hz (P15/60) demonstram que o uso do agitador eletromagnético em aços de grão não orientado com 2 % de silício é benéfico. O efeito de manutenção dos valores de J50 com o uso da agitação quando a temperatura de recozimento final aumenta, é particularmente importante durante a produção industrial para obter: alta polarização e baixa perda magnética, não observada na condição sem agitação.
dc.description.abstractotherThe influence of electromagnetic stirring during solidification in the continuous casting process was evaluated for a non-oriented electrical steel with 2 % silicon. Hot band samples from slabs with stirring (46 % equiaxed grains) and without stirring (15 % equiaxed grains) were submitted in the laboratory to hot band annealing at 1000 °C, cold rolling to a final thickness of 0.50 mm, and final annealing at temperatures between 860 °C and 1100 °C. Properties such as core loss and magnetic polarization were measured in the samples after the final annealing. Optical metallography, X-ray diffraction, and Electron Back-Scattering Diffraction (EBSD) were used for microstructural and texture evolution evaluation. The evaluation of magnetic properties was performed using the single sheet accessory for measuring magnetic core loss and polarization. Regarding the hot band grain size and the final grain size as a function of the use of electromagnetic stirring, the results were similar. When the hot band annealing was applied, the samples with the use of stirring showed preferential grain growth. Furthermore, the use of electromagnetic stirring demonstrated differences in the volume fraction of the main fibers (α, γ, η and θ) at all process stages. The results on magnetic properties, such as magnetic polarization (J50) and core loss at 1,5 T and 60 Hz (P15/60), demonstrate that the use of electromagnetic stirring in non-oriented electrical steels with 2 % silicon is beneficial. The effect kept in the J50 values with the use of electromagnetic stirring when the final annealing temperature increases, is particularly important during industrial production to obtain: high polarization and low magnetic core loss, not observed in the condition without stirring.
dc.identifier.urihttps://repositorio.cefetmg.br//handle/123456789/1333
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia de Materiais
dc.subjectAço elétrico (Propriedades magnéticas)
dc.subjectLigas de ferro silício
dc.subjectEngenharia de materiais
dc.titleAnálise do efeito da agitação eletromagnética sobre a evolução microestrutural, textura e propriedades magnéticas de um aço elétrico de grão não orientado com 2% de silício
dc.typeDissertação

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Análise do efeito da agitação eletromagnética sobre a evolução microestrutural, textura e propriedades magnéticas de um aço elétrico de grão não orientado com 2% de silício.pdf
Tamanho:
10.81 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.39 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia de Materiais