Estudo do efeito da transformação martensítica no comportamento mecânico do aço AISI 430 sob diferentes trajetórias de deformação

Página do item simplificado
dc.contributor.advisorLopes, Wellington
dc.contributor.advisor-coCorrêa, Elaine Carballo Siqueira
dc.contributor.advisor-coLatteshttp://lattes.cnpq.br/3203046752707862
dc.contributor.advisorLatteshttp://lattes.cnpq.br/4445376135095677
dc.contributor.authorSantos, Bruna Luíza dos
dc.contributor.authorLatteshttp://lattes.cnpq.br/4604869902728317
dc.contributor.refereeLopes, Wellington
dc.contributor.refereeCorrêa, Elaine Carballo Siqueira
dc.contributor.refereePaiva, Paulo Renato Perdigão de
dc.contributor.refereePereira, Pedro Henrique Rodrigues
dc.date.accessioned2025-03-19T22:46:18Z
dc.date.available2025-03-19T22:46:18Z
dc.date.issued2019-02-18
dc.description.abstractA mudança na trajetória de deformação, proveniente da combinação de esforços mecânicos durante um processo de conformação, pode influenciar na resposta mecânica de muitas ligas metálicas, que dependerá do processamento mecânico imposto e das particularidades estruturais da liga. Apesar do aço inoxidável AISI 430 ser ferrítico, austenita pode ser obtida em sua microestrutura em elevadas temperaturas, tornando-o apto a sofrer endurecimento devido à formação de martensita durante o tratamento térmico de têmpera. O comportamento mecânico do aço inoxidável ferrítico AISI 430, em função da mudança da trajetória de deformação com tratamentos térmicos, foi estudado. Neste caso, chapas de aço inoxidável ferrítico AISI 430 foram caracterizadas por meio de ensaios de tração, cisalhamento, dureza Vickers, ensaio metalográfico e difração de raios X, em seu estado inicial e após tratamentos térmicos de recozimento e de têmpera. Amostras foram recozidas, pré-deformadas (em tração, em cisalhamento, em cisalhamento direto-reverso, em laminação e em combinação de laminação com cisalhamento), tratadas termicamente em têmpera e, posteriormente, tracionadas e/ou cisalhadas. O tratamento térmico de têmpera promoveu a formação de martensita no aço AISI 430, aumentando a resistência mecânica e diminuindo a ductilidade do material, mesmo quando foi imposta pré-deformação ao aço antes da têmpera. Verificou-se a ocorrência de amaciamento quando o aço foi submetido a carregamentos do tipo cisalhamento direto/cisalhamento reverso, com a realização de têmpera entre os carregamentos. De forma geral, quanto menor a quantidade de pré-deformação imposta, maior a resistência mecânica do aço AISI 430 após o tratamento térmico de têmpera, indicando que a menor densidade de discordâncias favoreceria a transformação martensítica. A escolha dos tipos de tratamentos térmicos e suas temperaturas, combinada com a escolha dos tipos de esforços mecânicos e da quantidade de pré-deformação imposta, ou a sua não imposição, vão depender do processamento necessário para a fabricação do componente e das propriedades mecânicas que serão exigidas do mesmo durante a sua aplicação.
dc.description.abstractotherChanges in the combination of mechanical efforts applied on metallic material during a forming process also changes the strain path. It influences on the mechanical behavior of many alloys, which depends on the mechanical processing applied and the structural particularities of the alloy. Although the AISI 430 stainless steel is ferritic, austenite can be obtained in its microstructure at high temperatures. Which makes possible increase the steel hardening by quenching, due to the formation of martensite. It was studied the mechanical behavior of the AISI 430 ferritic stainless steel after different combinations of strain path and heat treatments. AISI 430 ferritic stainless steel sheets were characterized using tensile, shear, Vickers hardness, metallographic and X-ray diffraction tests. The steel was characterized as received and after annealing and quenching. Samples were annealed, pre-deformed (tensile, shear, straight-reverse shear, cold rolling and combination of cold rolling with shear), heat treated in quenching and, after, tensile tested and/or shear tested again. The quenching heat treatment promoted the formation of martensite in the AISI 430 steel, increasing its mechanical strength and decreasing its ductility, even when the steel was pre-deformed before the quenching. Material softening occurred when straight-reverse shear efforts were applied with the quenching heat treatment between the loadings. In general, the lower the amount of pre-deformation imposed, the higher the mechanical strength of the AISI 430 steel after the tempering heat treatment. Which indicates that the lower density of discordances favors the martensitic transformation. The choice of types of heat treatments and their temperatures, combined with the choice of types of mechanical stresses and the amount of pre-strain imposed (or its non-imposition) will depend on the processing required to manufacture the component and on the mechanical properties that shall be required during its application.
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior - Brasil (CAPES) - Código de Financiamento 001.
dc.identifier.urihttps://repositorio.cefetmg.br//handle/123456789/870
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia de Materiais
dc.subjectAço inoxidável ferrítico
dc.subjectDeformação plástica
dc.subjectTêmpera
dc.subjectCisalhamento
dc.titleEstudo do efeito da transformação martensítica no comportamento mecânico do aço AISI 430 sob diferentes trajetórias de deformação
dc.typeDissertação

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Estudo do efeito da transformação martensítica no comportamento mecânico do aço AISI 430 sob diferentes trajetórias de deformação.pdf
Tamanho:
6.65 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.39 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia de Materiais