Aglomerante de baixo carbono a partir da cinza de cavaco de eucalipto e sílica ativa

Página do item simplificado
dc.contributor.advisorBezerra, Augusto Cesar da Silva
dc.contributor.advisorLatteshttp://lattes.cnpq.br/0783179484317105
dc.contributor.authorLara, Luis Felipe dos Santos
dc.contributor.authorLatteshttp://lattes.cnpq.br/8256159827074633
dc.contributor.refereeCorrêa, Elaine Carballo Siqueira
dc.contributor.refereeAguilar, Maria Tereza Paulino
dc.contributor.refereeRezende, Domingos Sávio
dc.date.accessioned2025-03-27T12:48:22Z
dc.date.available2025-03-27T12:48:22Z
dc.date.issued2016-04-27
dc.description.abstractA cinza de cavaco de eucalipto (CCE) é um dos principais resíduos provenientes das termelétricas e um dos mais volumosos resíduos sólidos produzidos pelas indústrias nacionais. Essas indústrias produzem anualmente milhões de toneladas de CCE a partir do processo de geração de energia. De acordo com a Indústria Brasileira de Árvores (2016), o consumo brasileiro de eucalipto em 2013, como lenha industrial, foi de 41.832.528 m³ gerando cerca de 4.183.528 m³ de cinzas. Como contribuição ao desenvolvimento sustentável, o objetivo do presente trabalho foi o desenvolvimento de um aglomerante alternativo a partir de resíduos da indústria, a CCE e a fuligem de filtro de forno de produção de ferro silício - Sílica ativa (SA). As cinzas utilizadas foram beneficiadas por meio da moagem no moinho de bolas planetário de alto desempenho. A CCE e SA foram caracterizadas por análise visual, microscopia eletrônica de varredura com espectrometria de raios X dispersivo em energia, espectrometria de fluorescência de raios X por energia dispersiva, difração de raios X, análise térmica diferencial e termogravimétrica, perda ao fogo, granulometria por difração de laser e análise de área superficial. Foram confeccionadas pastas e argamassas com diferentes proporções de CCE (40, 50 e 60%), SA (60, 50 e 40%) e soluções alcalinas de hidróxido de sódio com concentrações de 0, 5, 10 e 15 mol/L. As pastas e argamassas foram caracterizadas microscopia eletrônica de varredura, difração de raios X, área superficial, porosidade e resistência à compressão. Os resultados obtidos para as propriedades mecânicas das pastas e argamassas soluções alcalinas de hidróxido de sódio com concentrações de 0, 5 e 10 mol/L foram satisfatórios. Os resultados de resistência à compressão corroboraram com os resultados de microscopia eletrônica de varredura, área superficial e porosidade. Foi apresentado o potencial do aglomerante desenvolvido em reduzir as emissões de CO2 na atmosfera quando comparado com concretos de cimento Portland convencionais.
dc.description.abstractotherEucalyptus chip ash (ECA) is one of the main residues from thermal power plants and one of the most voluminous solid residues produced by national industries. These industries produce millions of tons of ECC every year from the energy generation process. According to the Brazilian Tree Industry (2016), Brazilian consumption of eucalyptus as industrial firewood in 2013 was 41,832,528 m³, generating around 4,183,528 m³ of ash. As a contribution to sustainable development, the aim of this work was to develop an alternative agglomerant from industrial waste, ECC and soot from iron silicon production furnace filters - Active Silica (AS). The ash used was processed by grinding in a high-performance planetary ball mill. The OHC and AS were characterized by visual analysis, scanning electron microscopy with energy dispersive X-ray spectrometry, energy dispersive X-ray fluorescence spectrometry, X-ray diffraction, differential thermal and thermogravimetric analysis, loss on ignition, granulometry by laser diffraction and surface area analysis. Pastes and mortars were made with different proportions of SCC (40, 50 and 60%), SA (60, 50 and 40%) and alkaline sodium hydroxide solutions with concentrations of 0, 5, 10 and 15 mol/L. The pastes and mortars were characterized by scanning electron microscopy, X-ray diffraction, surface area, porosity and compressive strength. The results obtained for the mechanical properties of the pastes and mortars with alkaline sodium hydroxide solutions at concentrations of 0, 5 and 10 mol/L were satisfactory. The compressive strength results corroborated the scanning electron microscopy, surface area and porosity results. The potential of the developed binder to reduce CO2 emissions into the atmosphere when compared to conventional Portland cement concretes was presented.
dc.description.sponsorshipConselho Nacional de Desenvolvimento Científico e Tecnológico (CNPQ) Fundação de Amparo à Pesquisa do Estado de Minas Gerais (FAPEMIG)
dc.identifier.urihttps://repositorio.cefetmg.br//handle/123456789/978
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.departmentDepartamento de Engenharia de Materiais
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia de Materiais
dc.subjectMaterial cerâmico
dc.subjectCréditos de carbono
dc.subjectCimento Portland
dc.subjectResíduos industriais
dc.titleAglomerante de baixo carbono a partir da cinza de cavaco de eucalipto e sílica ativa
dc.typeDissertação

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Aglomerante de baixo carbono a partir da cinza de cavaco de eucalipto e sílica ativa.pdf
Tamanho:
9.64 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.39 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia de Materiais