Análise de corrosão do aço duplex UNS S31803 após os processos de conformação e soldagem

Página do item simplificado
dc.contributor.advisorPinheiro, Ivete Peixoto
dc.contributor.advisor-coSilva, Sidney Nicodemos da
dc.contributor.advisor-coLatteshttp://lattes.cnpq.br/7979338384555091
dc.contributor.advisorLatteshttp://lattes.cnpq.br/6117501358477717
dc.contributor.authorMota, Gabriela Leite
dc.contributor.authorLatteshttp://lattes.cnpq.br/0719949615864724
dc.contributor.refereePinheiro, Ivete Peixoto
dc.contributor.refereeSilva, Sidney Nicodemos da
dc.contributor.refereeLopes, Wellington
dc.contributor.refereeDumont, Marcello Rosa
dc.date.accessioned2025-03-25T19:44:25Z
dc.date.available2025-03-25T19:44:25Z
dc.date.issued2018-08-29
dc.description.abstractO aço inoxidável duplex UNS S31803 é um aço comercial que vem sendo bastante utilizado para aplicação nos setores de óleo e gás devido à sua alta resistência mecânica e corrosiva. Neste trabalho, o objetivo foi avaliar o efeito da conformação e soldagem, na microestrutura e na resistência à corrosão do material. Foram utilizadas chapas de aço duplex UNS S31803 com 1,8mm cedidas pela empresa Aperam South América. As chapas foram conformadas a frio por dobramento com um ângulo de 90°. Após o dobramento as peças receberam um cordão de solda por simples deposição pelo processo de soldagem TIG -Tungsten Inert Gas, com um aporte térmico de 0,4kJ/mm, realizado na ESAB. Para análise do material nas três condições estudadas, material como recebido (MR), material conformado (MC) e material conformado e soldado (MS), foram realizados ensaios de caracterização (MO/MEV), difração de raios X, quantificação da fração volumétrica da fase ferrítica com auxílio de um ferritoscópio e por análise de imagem. Para análise das propriedades corrosivas, foram aplicados ensaios de polarização potenciodinâmica cíclica no material nas três condições estudadas. Para o material deformado e soldado, a fração volumétrica de ferrita na zona termicamente afetada aumentou 49,7(±7,1) para 68,9(±4,0) indicando a maior formação dessa fase no material processado. Não foram observadas a formação da fase sigma, porém houve a formação de precipitados com morfologia compatível a nitretos de cromo na ferrita, o que indica à alta taxa de resfriamento após soldagem. Nos ensaios de polarização cíclica, foi constatado que o processo de soldagem do material conformado prejudicou seu desempenho quanto à sua resistência à corrosão, afetando a regeneração da película passiva.
dc.description.abstractotherThe stainless steel duplex UNS S31803 is a commercial steel that has been widely used for application in the oil and gas sectors due to its high mechanical and corrosive resistance. In this work, the objective was to evaluate the effect of the conformation and welding, in the microstructure and in the corrosion resistance of the material. UNS S31803 1,8mm duplex steel plates were used, provided by Aperam South America. The sheets were cold formed by folding at a 90 ° angle. After the bending the pieces received a weld bead by simple deposition by the welding process TIG -Tungsten Inert Gas, with a thermal input of 0.4kJ/mm, realized in ESAB. For the analysis of the material in the three studied conditions, material as received (MR), shaped material (MC) and shaped and welded material (MS), characterization tests (MO / MEV), X-ray diffraction, quantification of volumetric fraction of the ferritic phase with the aid of a ferritoscope and by image analysis. To analyze the corrosive properties, cyclic potentiodynamic polarization tests were applied to the material in the three conditions studied. For the deformed and welded material, the volumetric fraction of ferrite in the thermally affected zone increased from 49,7 (± 7,1) to 68,9 (± 4,0) indicating the higher formation of this phase in the processed material. No formation of the sigma phase was observed, but the formation of precipitates with morphology compatible to chromite nitrides in the ferrite was observed, indicating the high cooling rate after welding. In the cyclic polarization tests, it was found that the welding process of the shaped material impaired its performance in terms of its resistance to corrosion, affecting the regeneration of the passive film.
dc.identifier.urihttps://repositorio.cefetmg.br//handle/123456789/943
dc.language.isopt
dc.publisherCentro Federal de Educação Tecnológica de Minas Gerais
dc.publisher.countryBrasil
dc.publisher.initialsCEFET-MG
dc.publisher.programPrograma de Pós-Graduação em Engenharia de Materiais
dc.subjectAço inoxidável duplex
dc.subjectHidrociclones
dc.subjectCorrosão
dc.subjectIndústria offshore de petróleo
dc.titleAnálise de corrosão do aço duplex UNS S31803 após os processos de conformação e soldagem
dc.typeDissertação

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Análise de corrosão do aço duplex UNS S31803 após os processos de conformação e soldagem.pdf
Tamanho:
4.15 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.39 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar

Coleções

Mestrado em Engenharia de Materiais